Aerospace Lubricants TRIBOLUBE-64RPC primary characteristic is that it has extremely low start run torques at -100§F, yet will operate at temperatures of 400§F for long periods of time. Tribolube-64 is nonreactive with strong acids, oxygen. fuels, and solvents. It is an excellent anti-wear, extreme pressure lubricant with long life. Although this lubricant is very inert, newly exposed rubbing surfaces of aluminum and magnesium may react with the greases under certain conditions.

TRIBOLUBE-64RPC is intended for use in small and large diameter ball, roller, needle, and plain bearings, threads, valves, gears, and screw actuators. It is compatible with most elastomers and plastic seals, gaskets and O-rings.

• Type of Lubricant: Fluorinated Polyether Grease

• Packaging: 2 Oz. Tube

• Temperature Range: -100 to 400 °F

• Unworked Penetration @ 77°F: 348

• Worked Penetration @ 60 Strokes: 343

• Evaporation 22 hrs @ 400°F: 10.11%

• Oxidation Stability 100 hrs @ 212°F: 0 psi

• Oxidation Stability 500 hrs @ 212°F: 0 psi

• Weld Point @ Load: 800+ kg

• Copper Corrosion 24 hrs @ 212°F: 1b

• Evaporation 22 hrs @ 250°F: 2.71%

• Oil Separation 30 hrs @ 250°F: 5.81%

• LOX Impact Sensitivity 20 impacts from 1100 mm: No Reaction

• Water Washout- 1 hr @ 105°F: 1.46%

• Load Wear Index: 222.36

• Last Non-Seizure @ Load/Wear Scar: 100/0.57 kg/mm

• Steel-on-Steel Wear @ 1200 rpm. 40 kg. 167°F. 1 hrs. 52100 steel: 0.80 mm

• Steel-on-Steel Wear @ 1200 rpm. 40 kg. 400°F. 1 hrs. 52100 steel: 0.91 mm

• High Temperature Performance @ 400°F. 10000 rpm. 5 lbs: NA hrs

• Low Temperature Torque @-100°F. Starting: 943 gm-cm

• Low Temperature Torque @-100°F. 60 min. Running: 176 gm-cm

• Low Temperature Torque @-65°F. Starting: 293 gm-cm

• Low Temperature Torque @-65°F. 60 min. Running: 195 gm-cm

• Film Stability and Steel Corrosion 168 hrs @ 212°F: Pass

• Resistance to Aqueous Solution 168 @ 77°F: Pass

• Fuel Stability @ 77°F: 0.21%

• Fuel Resistance 8 hrs @ 77°F: Pass

• Type: 64